Rail steel has a considerably higher carbon content (0.7-0.8%), and hence is more brittle than mild steel. A variety of stress concentrating defects in rails, combined with the alternating loads from the passage of traffic, can produce slowly propagating fatigue crack. When this crack attains a critical size it causes an almost instantaneous brittle fracture…